Flame-retardant TPE / TPE-S flame retardant
11R80-101
Flame-retardant TPE for extrusion (11R) and injection molding (12R), including cable jackets and insulation.
Material data
11R80-101: 105℃ cable jackets
Grade overview
| Test Items | 11R80-101 |
|---|---|
| Hardness (Shore A / D) | 80A |
| Density (g/cm³) | 0.99 |
| MFR 190℃/5kg (g/10min) | 2.4 |
11R80-101
| Test Items | Condition | Units | Standard | Typical value | Test Method |
|---|---|---|---|---|---|
| Hardness | Shore A,15S | A | — | 80 | ASTM D2240 |
| Specific gravity | — | g/cm³ | — | 0.99 | ASTM D1238 |
| MFR | 190℃/5kg | g/10min | — | 2.4 | ASTM D1238 |
| Thermal Deformation | 150℃/4h | % | ≤50 | 15 | GB/T 2951.31 |
| Brittle point | -40℃ | Failures | ≤15/30 | 0/30 | GB/T 5470-2008 |
| Tear Strength | — | N/mm | 20 | 32 | K175 |
| Volume resistivity | 20℃ | Ω·m | ≥1.0×10¹² | 1.0×10¹⁴ | GB/T 1410-2008 |
| Tensile Strength | — | MPa | 10.0 | 16.0 | GB/T 1040-2006 |
| Elongation at break | — | % | 300 | 620 | GB/T 1040-2006 |
| Air-oven ageing · Tensile change | 135±2℃/168h | % | ±25 | +4 | GB/T 2951.12 |
| Air-oven ageing · Elongation change | 135±2℃/168h | % | ±25 | -11 | GB/T 2951.12 |
| Acid resistance · Tensile change | 45g/L H₂C₂O₄,23±5℃/168h | % | ±40 | 0 | GB/T 2951.21 |
| Acid resistance · Elongation change | 45g/L H₂C₂O₄,23±5℃/168h | % | ±40 | -4 | GB/T 2951.21 |
| Sodium hydroxide solution · Tensile change | 45g/L NaOH,23±5℃/168h | % | ±40 | 2 | GB/T 2951.21 |
| Sodium hydroxide solution · Elongation change | 45g/L NaOH,23±5℃/168h | % | ±40 | -7 | GB/T 2951.21 |
| Hot-water resistance · Tensile change | 80±2℃/168h | % | ±40 | 0 | GB/T 2951.21 |
| Hot-water resistance · Elongation change | 80±2℃/168h | % | ±40 | -1 | GB/T 2951.21 |
| Jacket shrinkage | 120℃/1h | % | 3 | 0 | GB/T 2951.13 |
| Crack resistance | 130℃/1h/10kg | — | No cracks | No cracks | GB/T 2951 |
| Damp-heat ageing · Tensile change | 85℃/85%RH/3000h | % | ±25 | +3 | GB/T 2951.12 |
| Damp-heat ageing · Elongation change | 85℃/85%RH/3000h | % | ±25 | -2 | GB/T 2951.12 |
The data shown are typical values, not guaranteed specifications. Actual properties may vary with processing conditions. Contact us to discuss material selection and application requirements.